Low Smoke Halogen Free Frame Retardent Compound for Power Cable

Introduction
EPchem® POHF-0702 is polyolefin based material containing inorganic flame retardant, antioxidant, lubricant, etc., produced by mixing, plasticizing and then pelletizing. POHF-0702 is appropriate for sheath of power cables, control cables, communication cables and so on.
POHF-0702 is excellent in mechanical properties, flame retardant performance (cables can pass mounted bunched wires or cables-Category C), low smoke, outstanding resistance to cracking and high temperature, good processability.

Characteristics *The data in the list above is typical value rather than the guarantee value.
Processing
POHF-0702 has good processing performance, can be well processed using PVC and Polyethylene standard extrusion screw, preferring a low compression ratio (1.2 ~ 1.8) screw for the best extrusion effect. In general we recommend the following processing conditions:

• Extruder L/D: 20~25
• Filter (mesh): 30~60
• Temperature setting:

     Zone1    Zone2    Zone3   Zone4    Zone5      Die
    110ºC   120ºC   135ºC  145ºC   150ºC   150~165ºC
The above temperatures are for reference only, but should be adjusted depending on specific equipment. But the melting temperature should not exceed 170ºC.
POHF-0702 includes black and natural color. Users are free to add color masterbatches to natural color material. The suggested weight ratio is 1.5% or so.

Storage
These compounds must be stored under the following conditions:

1. closed and undamaged bags
2. ambient temperature does not exceed 45ºC
3. avoid direct exposure to sunlight and weathering
4. shelf life:12 months.

Package
To be packed in aluminum foil bag inside and kraft paper bags outside, 25kg net each; or damp-proof cabinets on pallet, 1000kg net each.






The workshop:


Package :


  Introduction
EPchem® POHF-0702 is polyolefin based material containing inorganic flame retardant, antioxidant, lubricant, etc., produced by mixing, plasticizing and then pelletizing. POHF-0702 is appropriate for sheath of power cables, control cables, communication cables and so on.
POHF-0702 is excellent in mechanical properties, flame retardant performance (cables can pass mounted bunched wires or cables-Category C), low smoke, outstanding resistance to cracking and high temperature, good processability.

Characteristics *The data in the list above is typical value rather than the guarantee value.
Processing
POHF-0702 has good processing performance, can be well processed using PVC and Polyethylene standard extrusion screw, preferring a low compression ratio (1.2 ~ 1.8) screw for the best extrusion effect. In general we recommend the following processing conditions:

• Extruder L/D: 20~25
• Filter (mesh): 30~60
• Temperature setting:

     Zone1    Zone2    Zone3   Zone4    Zone5      Die
    110ºC   120ºC   135ºC  145ºC   150ºC   150~165ºC
The above temperatures are for reference only, but should be adjusted depending on specific equipment. But the melting temperature should not exceed 170ºC.
POHF-0702 includes black and natural color. Users are free to add color masterbatches to natural color material. The suggested weight ratio is 1.5% or so.

Storage
These compounds must be stored under the following conditions:

1. closed and undamaged bags
2. ambient temperature does not exceed 45ºC
3. avoid direct exposure to sunlight and weathering
4. shelf life:12 months.

Package
To be packed in aluminum foil bag inside and kraft paper bags outside, 25kg net each; or damp-proof cabinets on pallet, 1000kg net each.






The workshop:


Package :


 

Razor Wire

Razor Wire,Barbed Wire,Galvanized Razor Wire

Kaian Metal Wire Mesh Co., Ltd. , http://www.hsweldedmesh.com